New composite based on polypyrrole (PPy) and bismuth oxide (α-Bi2O3) was investigated as supercapacitor electrode. The α-Bi2O3 was obtained by hydrothermal route at 500 ºC for 2 h. Cyclic voltammetry was used to electropolymerize PPy on graphite electrode (GE) or on GE/α-Bi2O3. The X-ray diffraction profile of Bi2O3 revealed the α-Bi2O3 monoclinic structure with space group P21/c.The scanning and transmission electron microscopy images showed that PPy coated α-Bi2O3. Raman spectra showed that PPy inhomogeneously coated α-Bi2O3, but it was still possible to obtain a α-Bi2O3 @PPy core-shell hybrid composite with highly ordered α-Bi2O3 with electronic interaction between the oxide and the polymer chain of the polymer. The GE/α-Bi2O3@PPy composite electrode (type I supercapacitor) displayed a predominantly capacitive profile with low impedance values and good electrochemical stability after 50 charge and discharge cycles. The specific capacitance of α-Bi2O3 @PPy composite was found in the range of 634 to 301 F g-1 to gravimetric current of 3 and 10 A g-1, respectively.

There are many controversies regarding the cyto- and genotoxicity of carbon nanotubes (CNTs). In this work, we discuss that many of the incongruous arguments are probably associated with the poor physical-chemical characterization of the CNT samples used in many publications. This manuscript presents examples of carbon nanostructures observed under high resolution electron microscopy that can be found in typical CNT samples, and shows which roles in cyto- and genotoxicity need to be better investigated. Issues concerning chemical treatment are addressed and examples of misunderstandings that can occur during the studies of cyto- and genotoxicity of CNT samples are given.

Materiais carbonaceos com diferentes estruturas são preparados da carbonização do bagaço da cana de açúcar. Os materiais obtidos são caracterizados utilizando-se microscopia de varredura eletrônica e técnicas eletroquímicas. Dependendo das condições de carbonização é possível obter fuligens ricas de partículas tipo flocos ou tipo colméia de abelha, cuja concentração tem grande influência sobre a armazenagem de lítio nos eletrodos. Para fuligens ricas de partículas do tipo colméia observa-se uma capacidade específica reversível da ordem de 310 mAh g-1. Os resultados sugerem que o bagaço da cana pode ser um percursor com potencial para o desenvolvimento de materiais anódicos para baterias de ions de lítio.

Carbonaceous materials with different structures are prepared by carbonization of sugarcane bagasse. Depending on carbonization conditions, it is possible to obtain soot rich in flakes or in honeycomb-shaped micrometric particles, whose concentration has large influence on lithium storage into electrodes. The soot rich in honeycomb-shaped particles provides the best electrochemical performance, with a reversible specific capacity of 310 mAh g-1. The results suggest that the sugarcane bagasse can be potentially used in the design of anodic materials for lithium ion batteries.

This paper presents the alkaline battery (MnO2/Zn) as a useful device in the teaching of chemistry. The preparation of the battery, the materials used in the preparation of the MnO2 electrode, the mechanism of energy storage and the parameters often used in the understanding of general batteries are discussed in detail. In addition, a schedule and a questionnaire that can be applied in an experimental class have been developed, which allow the assembly of an alkaline battery, its discharge using a galvanostatic or a load-resistance procedure, and the elaboration of a report based on the main text. This experimental class has been offered in the chemistry course of FFCLRP.